Przybylski, M., Grabowski, J., Wulfhekel, W., Rams, M., Tomala, K., Kirschner, J.

Magneto-optical properties of Fe/Cr/Fe/MgO/Fe structures epitaxially grown on GaAs(001)
Journal of Applied Physics 95, (2),pp 597-602 (2004)
Fe/Cr/Fe trilayers were epitaxially grown on atomically flat GaAs(001). For the thickness of Cr spacer layer corresponding to antiferromagnetic coupling, "reversed" minor hysteresis loops were measured with longitudinal magneto-optical Kerr effect (MOKE), i.e., a negative "magnetization" signal was detected when the thicker bottom Fe layer was saturated along the applied field. This behavior is interpreted by depth variations of the MOKE sensitivity. Magnetization reversal shows that both antiferromagnetic switching and spin-flop transition fields depend on the ratio of both Fe film thicknesses. The shape of the MOKE loops becomes more complex with further deposition of MgO and Fe layers on the top of the Fe/Cr/F/GaAs(001) stack. Superconducting quantum interference device measurements confirm the interpretation of the MOKE loops and demonstrate homogeneity and sharpness of the interfaces in the structures.